PRODUCT NAME :
bearing steel
STANDARD:
GB/T18254-2002 ISO683-17
GRADE COMPARISION:
|
GB |
ГОСТ |
ASTM |
BS |
JIS |
NF |
DIN |
|
GCr15 |
ШX15 |
E52100 |
534A99 |
SUJ2 |
100C6 |
100Cr6 |
ULTRASONIC STANDARD:
GB/T6402-2008 / SEP921-84. ASTM A388
CHEMICAL COMPOSITION:
|
C |
Si |
Mn |
P≤ |
S≤ |
Cr |
|
0.95/1.05 |
0.15/0.35 |
0.25/0.45 |
0.025 |
0.025 |
1.40/1.65 |
HEAT TREATMENT SPECIFICATION:
Annealed .
Common anneaing :790-810℃，furnace cooling to 650℃ HB170-207
MECHANICAL PROPERTIES:
Hardness (HRC):25.8
Tensile strength (MPa):861.3
Yield strength (MPa):518.42
Elongation :(%):27.95
DELIVERY CONDITION :
annealed
DIMENSION : mm
|
ROUND STEEL BAR |
COIL ROD |
WIRE |
SQUARE/ FLAT |
|
FORGED BAR |
ROLLED BAR |
HOT ROLLED |
COLD DRAW |
FORGED |
ROLLED |
|
100-700 |
16-250 |
∮5.5-20 |
∮0.2-13 |
120-800×120-800 |
5-38×44-150 10-90×60-305 |
APPLIED RANGE:
Bearing steel is the general term for alloy steel used in the manufacture of bearing races and moving parts of all types of
roller bearings. High carbon and chromium bearing steel is widely applied in the manufacture of pin rollers and sleeves on
driving shaft used in auto components, construction machinery, combustion engines, electric locomotive, machine tools,
tractors, steel rolling equipment, and drilling and exploration equipment for mining industry. Carburized bearing steel is mainly
used in railway locomotives and wind turbines. The high-grade bearing steel products developed with proprietary technology
have been highly appraised by six leading bearing manufacturers in the world.
REMARK：
Above listed parameters and sepcification only for reference . Specific parameters according to standard. Requirments beyond
standard will be negotiate by both sides .
Delivery state:annealed, spheroidal annealed, quenched & tempered ,bright bar, cold-drawn, etc.
Listed specifications are only typical grades; products of required specifications can be developed/produced per international,
Chinese or industry standards, or based on agreements with customers.